Inspection techniques The principle of the eddy current method is that a determined energy flux is induced into the material to be tested with an EC-probe by generating a magnetic field which penetrates the material causing eddy currents. Any defects or irregularities in the grain structrure disturb the energy flow leading to indications on the oscilloscope. View animation of eddy-current (1.012kB) >

	System calibration View animation of calibration (1.593kB) >

	Inspection Procedure Overview View animation of inspection procedure (1.732kB) >

	Result Documentation View single chars of our result documentation (html) >

HOME

Eddy current testing, non destructive testing, Eddy current tests: Reformer tube testing, catalyst tube inspection, testing of centrifugal casting tube, Reformer pipes, Reformer tubes, pipes, plants, hydrogen, methanol, ammonia, Reformer pipe tests, Hydrogen reformer inspection, Refinery Plants, Refining and Chemical Plants, Methanol Plant, Amnonia Plant, Power plants, NDT Inspection, catalyst tubes, crack, tube expansion, rupture, non destructive testing of reformer tubes, eddy current testing of reformer tubes, Eddy current test of: Reformer pipes, Reformer tubes, Reformer tube inspection, Reformer tube tests, Reformer tube test, Reformer pipe tests, testing of centrifugal casting tubes, Life time assessment of reformer tubes, centrifugal casting tube testing, Hydrogen reformer, Refinery Plants, Refining and Chemical Plants, Methanol Plant, Ammonia Plant, Hydrogen Plant, Fertilizer plant, Chemical Plant, Methanol Plants, Ammonia Plants, Hydrogen Plants, Fertilizer plants, NDT Inspection, crack testing, catalyst tubes, tube expansion, creep failure, rupture, catalyst tube, cracks, creep failures, crack detection, crack test, metal sorting, tube inspection, wheel inspection,Reformer Tubing Inspection, hydrogen reformer, Furnace Tubing Inspection, Field Services, NDT Inspection Companies, NDT Inspection Services, catalyst, catalyst cracking, cracking, creep, creep expansion, creep damage, creep failure, creep testing, metal dusting, thermal expansion, catalyst dusting, tensile damage, tensile rupture, tensile stress, rupture, high temperature oxidation, oxidation, high temperature sulfidation, sulfidation, high temperature carbonization, carbonization, hot corrosion, thermodynamic stability, end of life techniques, NDE Services, nondestructive examination, Automated NDT Instrumentation, Nondestructive Evaluation, Finned Exchanger Tubing, Air conditioning, CoGeneration, Condenser Tubes, Corrosion Cracking, Defects, Deformation, Erosion, Geothermal, Heat Exchanger Tubes, Heat Recovery Steam Generator, Pitting, Power Generating Plants, Preventative Maintenance, Recovery Boiler, Small Bore Tubing, Vaporizer Tubes, gas, eddy current method, Material Analysis and Testing